    Epoxy Linking Paint


    Epoxy Linking Paint


    Characteristic: Excellent flexibility, shielding, low water permeability and temperature dry, can be cured under -10°C, perfect adhesion with nonferrous metal.

    Usage: mainly as the transition primer for anti-fouling paint of bottom, and it is also used on the surface of non-ferrous paint.

    Detailed specification:

    Mixing ratio: Main agent/Firming agent=8/1(by weight)

    Temperature°C

    Dry to touch min

    Dry semi-hard hrs

    Min. interval hrs

    Max. interval d

    -10  0   10    20    30

    4    2.5   2   1.5     1

    36   24  18    12    10

    36   24  18    12    10

    Standard thickness: Dry: 40μm/coat

    Academic spreading rate: 0.12kg/ m2/40μm

    Solid contents: 67%

    Humidity requirement: below 85%

    Drying time & Coating interval

    Substrate Treatment

    Bare steel surface must abrasive blasted and anti rust, conforms to ISO Sa2.5 grade, aluminum material,zinc material surface should be clean and dry,no feculence and remove zinc salt, primers surface must dry, without feculence.

    Matching

    Applicable substrate: unpainted steel,zinc material,aluminum material or sprayed kinds of zinc powder paints and surface of bilge anti-corrosive paint.

    Applicable upper coatings: kinds of polyurethane,epoxy or bilge anti-fouling paint,chlorination rubber paint etc.