Hot Rolled High-Strength FH36 Steel Plate for Shipbuilding
Hot rolled high-strength FH36 steel plate for shipbuilding is a kind of high strength naval steel plate, which is Equivalent Steel Grades of CCS FH36, AB/FH36, AB/FH36N, BVFH36,NV F36, GL-F36, GL-F36TM, KRFH36, LRFH36 and RINA-FH36. The plate is conducted impact test in the case of -60℃. FH36 shipbuilding steel plates can be used in the manufacture of the ship's hull structure whose weight is below 10000 tons.
If you have any interest, please feel free to contact us!
Stock Sizes
Thickness Range：1.5 to 150 mm
Width Range：1500 to 2200 mm
Length Range：3000 to 18000 mm
Parameters for Hot rolled High-strength FH36 steel plate for shipbuilding
|
Project |
Data |
||
|
Steel Grade |
FH36 |
||
|
Chemical Composition |
C % |
≦0.16 |
|
|
Si % |
≦0.50 |
||
|
Mn % |
0.90~1.60 |
||
|
P % |
≦0.020 |
||
|
S % |
≦0.020 |
||
|
Cu % |
≦0.35 |
||
|
Cr % |
≦0.20 |
||
|
Ni % |
≦0.80 |
||
|
Nb % |
0.02~0.05 |
||
|
V % |
0.05~0.10 |
||
|
Ti % |
≦0.02 |
||
|
Mo % |
≦0.08 |
||
|
N % |
≦0.009 |
||
|
Mechanical Property |
Upper Yield strength (ReH/MPa) |
≧355 |
|
|
Tensile Strength (Rm/MPa) |
490~630 |
||
|
Elongation after Fracture (A/%) |
≧21 |
||
|
Charpy V-Notch Impact Test |
Thickness: ≦50mm |
Longitudinal (KV2/J) |
34 |
|
Transverse (KV2/J) |
24 |
||
|
Thickness: >50~70 |
Longitudinal (KV2/J) |
41 |
|
|
Transverse (KV2/J) |
27 |
||
|
Thickness: >70~150 |
Longitudinal (KV2/J) |
50 |
|
|
Transverse (KV2/J) |
34 |
||
|
Test Temperature (℃) |
-60
|
||